High performance Monofrax s-3
Fused cast zirconia corundum bricks for Glass furnace
Features of monofrax s-3 s-4 s-5 Fused cast zirconia corundum bricks :
1. Raw material is corundum and baddeleyite eutecticum,high compression strength
2.Top high-temperature capablility,excellent thermal stability.
3.Strong resistant erosion stability to the glass liquid
physical and chemical index of monofrax s-3 s-4 s-5 AZS bricks Fused cast zirconia corundum bricks
| ITEMS | AZS-41 | AZS-36 | AZS-33 | |
| ZrO2 (%) ≥ | 40.5 | 35.5 | 32.5 | |
| SiO2 (%) ≤ | 13 | 14 | 16 | |
| Al2O3 (%) ≥ | 45 | 49 | 50 | |
| Na2O (%)≤ | 1.3 | 1.4 | 1.5 | |
| Fe2O3+TiO2 (%) ≤ | 0.3 | 0.3 | 0.3 | |
| B.D. (g/cm 3 ) ≥ | 4 | 3.85 | 3.75 | |
| C.C.S (Mpa) ≥ | 350 | 350 | 350 | |
| Apparent density(g/cm 3 ) | PT/QX | 3.55 | 3.45 | 3.4 |
| ZWS | 3.9 | 3.65 | 3.6 | |
| WS | 3.92 | 3.78 | 3.7 | |
| Apparent Porosity (%) | 1.3 | 1.5 | 2 | |
| Refractoriness ( C) | 1730 | 1710 | 1710 | |
| 0.2Mpa Softening temp. under load( C) | >1700 | >1700 | >1700 | |
| Exudation temp. of Glass Phase( C) | >1430 | >1420 | >1400 | |
| Corrosion Resistance of Glass Melt(mm/24h) | 1.1 | 1.2 | 1.3 | |
| Thermal Expansion(%), 100C | 0.8 | 0.8 | 0.8 | |
| Glass Phase (%) | 18 | 19 | 20 | |
Casting method of monofrax s-3 s-4 s-5 Fused cast zirconia corundum bricks :
Electrocast zirconia corundum block is made by completely melting the raw materials and casting it in a casting mold, which is cooled and solidified. The shrinkage caused by the volume shrinkage of this product during condensation is a matter of special attention when using it. The casting methods of fused zirconium corundum bricks are ordinary casting (PT), inclined casting (QX), non-shrinkage casting (WS) and quasi-shrinkless casting (ZWS)
Usage of monofrax s-3 s-4 s-5 Fused cast zirconia corundum bricks
Fused Cast zirconia corundum are widely used in glass melting furnace because the fused zirconium corundum brick is an important refractory material variety in modern glass melting furnaces. It is currently produced in a large amount in the world. It is a widely used refractory product. It has good resistance to glass erosion and resistance to rapid cooling and heat. The heat load performance is applied to all important parts of the furnace.
PT: The usual pouring method, the shrinkage hole of the product is located in the lower part of the casting mouth, and it is mostly used for the upper structure of the melting pool.
QX: The oblique casting method is adopted, and the shrinkage hole of the product is offset to the lower end, which is mainly used as a pool wall brick.
WS: Non-shrinkage casting, the non-shrinkage product of the shrinkage hole part of the cast brick is mainly used, such as the liquid erosion hole, the kiln sill, the corner of the pool wall, the paving surface, etc.
ZWS: Quasi-free shrinkage casting, mainly used as pool wall bricks, basically removing the shrinkage of the cast bricks, mainly used as pool wall bricks.
1. Strong professional:
Our company has thirty years producing experience in refractory product. Our manager will supervise on a various refractory' s production materials, process control, quality supervision and package delivery, and ensure the products are 100% qualified.
2. Annual exports:
Now we have gained a global sales network reaching Taiwan, Russia, Mongolia, South Korea, Vietnam, Pakistan, Bulgaria, Finland, Greece, Spain, Congo, Angola, South Africa, and Maldives, Jordan and so on. The export figure is more than USD 4 million.
3. Production equipment:
Production and testing equipments are new, complete and automated or semi- automated. Such modern facilities and equipments have provided the fine technical guarantee for the production and testing.
4. Testing equipment;
Our company's testing equipments as follows:
High Temperature RUL Tester
Bulk Density Tester
The Pressure Tester
Refractoriness Tester